UV adhesive for button transfer and bonding of mobile phone

Item No.

Products' features and typical usage

3343

Strong adhesion for PC to PET, can pass the cross-cut test, bending with 180 degree, it won't be cracked, bended, peeled off; Have excellent performance of resistance to high temperature, low temperature, waterproof, Chemical solvents and uv resistance. Dedicated to the transfer and coating of PC and PET button. The Glue will be Keypad after UV curing.

3323

Resistance to the environment-friendly testing, no white color, high adhesive strength with wide range of applicability; have high bonding strength to all kinds of oil ink or electroplating buttons; Have excellent performance of high temperature resistant, low temperature resistant, high humidity resistant; Suitable for the bonding of silica gel to metal, PC, ABS, oil ink coating, electroplating materials and others. Typically applications in the industry of mobile phone, digital camera, medical equipment.

3328

(A+B)

Two-component ratio, working time can up to 12hours; Resistance to the environment-friendly testing, no white color, high adhesive strength with wide range of applicability; Have excellent performance of high temperature resistant, low temperature resistant, high humidity resistant; Suitable for the bonding of silica gel to metal, PC, ABS, oil ink coating, electroplating materials and others. Typically applications in the industry of mobile phone, digital camera, medical equipment.

3325

Good adhesion to TPU material, the applicability range is wide, and have a high adhesive strength to all kinds of oil ink and Electroplating buttons; suitable for the bonding of TPU to PC or ABS, ink coating, electroplating, metal and other materials; Typically applications in the button industry of mobile phone, digital camera, mechanical equipment.

Status

Parameters Name

Technical parameters

3343

3323

3328(A+B)

3325

Before UV curing

Liquid Color

Clear liquid

Clear and colorless liquid

light yellow liquid

Clear light yellow liquid

Viscosity(cps, tested under 25℃)

400-1000

250

4500-5500（A）

2200-2800

Proportion (g/cm3)

1.08

1.09

1.08

1.08

PH value

6

6

6

7

During UV curing

setting time/sec'

6

15

5

2

Solid energy (mj/cm2)

1500

1500-2000

1800

1200

After UV curing

Hardness

Shore A

/

/

/

/

Shore D

76

68

60

72

Pencil

B

/

/

/

Shrinkage rate(%)

3

3

3

3

Bibulous rate(%)

1.0

1.5

2

1.5

temperature-resistant scope(℃)

-5~150

-5~150

-5~150

-5~150

Polymer content(%)

100%

100%

100%

100%

Tensile strength (MPa)

>14

>14

>14

>14

Shear strength (MPa)

/

/

/

/

Peel strength (Kgf/cm2)

/

/

/

/

Elongation at break

/

/

/

/

Light transmittance (%)

/

/

/

/

Refractive index

/

/

/

/

Elastic modulus

/

/

/

/

Dielectric constant (1MHz)

3.9

3.9

3.9

3.9

Dielectric loss(1MHz)

0.03

0.03

0.03

0.04

Dielectric strength (KV/MM)

27

27

30

26

Surface resistivity(Ω.cm)

0.8 x 1016

0.8 x 1016

0.8 x 1016

0.8 x 1016

Volume resistivity(Ω.cm)

1.3 x 1016

1.3 x 1016

1.3 x 1016

1.3 x 1016

Spec

1KG/bottle

Shelflife

One Year(Seal storage and comply with storage conditions.)

Notes

1. Storage under 8℃－25℃, in the dark, sealing, ventilation, cool conditions, and far away from children.

2. Keep air ventilation when using, and take the safe protection measures, such as don't use your skin to touch the resin directly or longly.

Remarks

1.) Viscosity standard： Tested under 25℃±0.5, by using the container with diameter 6-7cm, and height 10cm.

2.) The setting time of above items were tested under the condition of glass bond glass  with 40w and light intensity is under 7.5mW/cm2.                                                                                                                                           3.) Above tensile & shear strength data tested when glass bond glass, glass bond crystal.

4.) Other test parameters are tested on the basis of the national testing.