UV glue for UV anaerobic double curing

Item No.

Products' features and typical usage

366

UV- anaerobic double curing, can be used for the mutual bonding of two opaque inorganic material;High strength, and effective to most inorganic material, can be used as a structure adhesive, good resistance to the high and low temperature, can go through the wave soldering, can speed up the curing of anaerobic if spray 355 primer first before apply the glue, the position can be fixed after jointing in 3min. Typical applications in micro-motor, buzzer industries, with opaque materials and one side is metal adhesion.

Status

366

Before UV curing

Liquid Color

Clear light yellow liquid

Viscosity(cps, tested under 25℃)

8000-15000

Proportion(g/cm3)

1.07

PH value

5.0

During UV curing

setting time/sec'

10~12

Solid energy(mj/cm2)

1500-2000

After UV curing

Hardness

Shore A

/

Shore D

45

Pencil

/

Shrinkage rate(%)

3

Bibulous rate(%)

2

temperature-resistant scope(℃)

-5~150

Polymer content(%)

100

Tensile strength (MPa)

17

Shear strength(MPa)

/

Peel strength (Kgf/cm2)

≥50

Elongation at break%

/

Light transmittance (%)

/

Refractive index

/

Elastic modulus

/

Dielectric constant (1MHz)

3.8

Dielectric loss(1MHz)

0.03

Dielectric strength (KV/MM)

19

Surface resistivity(Ω.cm)

6.2×1015

Volume resistivity(Ω.cm)

6.9×1015

Spec

500g/bottle

Shelflife

One Year(Seal storage and comply with storage conditions.)

Notes

1. Storage under 8℃－25℃, in the dark, sealing, ventilation, cool conditions, and far away from children.

2. Keep air ventilation when using, and take the safe protection measures, such as don't use your skin to touch the resin directly or longly.

Remarks

1.) Viscosity standard： Tested under 25℃±0.5, by using the container with diameter 6-7cm, and height 10cm.

2.) The setting time of above items were tested under the condition of glass bond glass  with 40w and light intensity is under 7.5mW/cm2.                                                                                                                                           3.) Above tensile & shear strength data tested when glass bond glass, glass bond crystal.

4.) Other test parameters are tested on the basis of the national testing.